Compact 2514

Summary

Product identification

• Model: COMPACT 2514
• Configuration: Spiral Wound
• Membrane Polymer: Composite Polyamide
• Brine Spacer Material: Polypropylene

Operating limits

• Maximum Operating Temperature: 113 °F (45 °C)
• Maximum Feed Flow: 6 gpm (23 lpm)
• Maximum Pressure Drop: 10 psi (0.7 bar)
• Maximum Chlorine Concentration: < 0.1 ppm
• Maximum Feedwater SDI (15min): 3.0
• Maximum Feedwater Turbidity: 0.5 NTU
• Feedwater pH Range: 3.0 ÷ 10.0
• Minimum ratio of concentrate to permeate flow: 5:1 (for any element)
• Operating Pressure: 180 psi (12.4 bar)

Feed water

Test conditions for performance data (after 30 min of operation):

• Solution: NaCl
• Applied Pressure: 150 psi (10.3 bar)
• Operating Temperature: 77 °F (25 °C)
• Permeate Recovery: 10%
• pH Range: 6.5 ÷ 7.0
• Specific conditions for LOW4 (*): NaCl 500 ppm, Applied Pressure 100 psi (6.9 bar)

Product water

• Nominal Membrane Area: 6 ft² (0.6 m²)
• Performance (at specified test conditions):
  • LOW1:
    • Permeate Flow: 185 gpd (0.7 m³/d)
    • Salt Rejection: 99.0% nominal (98.0% minimum)
  • LOW2:
    • Permeate Flow: 120 gpd (0.5 m³/d)
    • Salt Rejection: 99.4% nominal (99.0% minimum)
  • LOW3:
    • Permeate Flow: 200 gpd (0.76 m³/d)
    • Salt Rejection: 98.5% nominal (97.0% minimum)
  • LOW4 (*):
    • Permeate Flow: 150 gpd (0.57 m³/d)
    • Salt Rejection: 99.0% nominal (98.0% minimum)
• Note: The test conditions with “ * “ refer to LOW4. Minimum permeate flow for individual modules may vary 15% below nominal.

Mechanical / hydraulic

• Dimensions:
  • Total Length (A): 16.40 inches (417 mm)
  • Partial Length (B): 13.25 inches (337 mm)
  • Max Diameter (C): 3.05 inches (77 mm)
  • Tubular Diameter (D): 2.75 inches (70 mm)
  • Dimension E: 5.1 inches (130 mm)
• Weight (shipped-working): 4.0-4.7 lbs (1.8-2.1 Kg)
• Configuration: No Vessel Required

Additional information

• Modules are sealed with small screws (to be removed when used).
• They contain less than 1.0% sodium meta-bisulfite and less than 10% propylene glycol solution.
• Packaged in a cardboard box.
• Size must be considered in a range of ±3% except for the lengths (A and B) ±3‰.
• Permeate obtained from the first hour of operation should be discarded.
• Avoid static permeate-side backpressure at all times.
• The presence of free chlorine and other oxidizing agents will cause membrane failure, and the damage is not covered under warranty.
• These membranes may be subject to drinking water application restrictions in some countries; please check the application status before use and sale.

---

Disclaimer: This summary is based on text extraction and may miss figures, footnotes, or revisions present in the original PDF. Contractual data must match the OEM PDF revision used on the project.