LOW4-2540

Summary

Product identification

• Model: LOW4-2540
• Description: Extra Low Energy, Excellent Productivity - Brackish Water Element
• Type: Spiral Wound
• Membrane Polymer: Composite Polyamide
• Brine Spacer Material: Polypropylene

Specifications

• Nominal Permeate Flow: 800 gpd (3,0 m³/d)
• Nominal Salt Rejection: 99,0% (98,0% minimum)
• Nominal Membrane Area: 28 ft² (2,6 m²)

Test Conditions

• NaCl Solution: 500 ppm
• Applied Pressure: 100 psi (6,9 bar)
• Operating Temperature: 77 °F (25 °C)
• Permeate Recovery: 10%
• pH Range (after 30 min of operation): 6,5 ÷ 7,0

Mechanical / hydraulic

• Length: 40.0 inches (1016 mm)
• Diameter: 2.4 inches (61 mm)
• Connection Diameter: 0.75 inches (19,1 mm)
• Core Tube Extension (Feed Side): 1.2 inches (30,5 mm)
• Core Tube Extension (Conc. Side): 1.2 inches (30,5 mm)
• Weight: 4 lbs (1,8 Kg)

Operating limits

• Maximum Operating Pressure:
  • Fiberglassed: 600 psi (41,4 bar)
  • Tape Wrapped: 300 psi (20,7 bar)
• Maximum Operating Temperature: 113 °F (45 °C)
• Maximum Pressure Drop: 10 psi (0,7 bar)
• Maximum Feed Flow: 6 gpm (23 lpm)
• Maximum Feed Chlorine Concentration: <0,1 ppm
• Feedwater pH Range: 3,0 ÷ 10,0
• Feedwater SDI (15min): 5,0
• Feedwater Turbidity: 1,0 NTU
• Minimum ratio of concentrate to permeate flow for any element: 5:1

Other Operating Information

• Minimum permeate flow for individual elements is 20 percent below listed flow.
• Elements are vacuum sealed in a polyethylene bag containing less than 1.0% sodium meta-bisulfite and 10% propylene glycol solution.
• Guidelines:
  • Permeate obtained from the first hour of operation should be discarded.
  • Avoid static permeate-side backpressure at all times.
  • These membranes may be subject to drinking water application restrictions in some countries; check application status before use and sale.
  • For element loading, use only glycerine to lubricate o-rings and brine seal.
• Warnings:
  • The customer is fully responsible for the effects of incompatible chemicals on elements.
  • The presence of free chlorine and other oxidizing agents will cause membrane failure, and the damage is not covered under warranty.

---